pk | doi | Contact name | Steel type | T /K | φ /m-2.s-1 | Γ /m-2 | Ion energy | Dtot /m-2 |
---|---|---|---|---|---|---|---|---|
R6091 | - | Golubeva | Eurofer | 443 | 3e+21 | 3e+24 – 7.3e+25 | - | - |
R6092 | - | Golubeva | Rusfer | 443 | 3e+21 | 3e+24 – 7e+25 | - | - |
R6093 | - | Golubeva | Rusfer | below melting | 1e+23 – 1e+24 [D pulsed high heat plasma loading, 0.3 MJ/m2, 1 ms] | in 1 pulse big uncertainity; 1 and 5 pulses (see "ion flux" column) | - | 1e+20 – 3.7e+20 |
R6094 | - | Golubeva | Eurofer | below melting | 1e+23 – 1e+24 [D pulsed high heat plasma loading, 0.3 MJ/m2, 1 ms] | in 1 pulse big uncertainity; 1 and 5 pulses (see "ion flux" column) | - | 1.3e+20 – 1.5e+20 |
R6095 | - | Golubeva | F82H | below melting | 1e+23 – 1e+24 [D pulsed high heat plasma loading, 0.3 MJ/m2, 1 ms] | in 1 pulse big uncertainity; 1 and 5 pulses (see "ion flux" column) | - | 4.8e+19 – 1.1e+20 |
R6101 | - | Golubeva | Rusfer | 600 | - | - | - | 7.6e+20 – 9e+20 |
R6100 | - | Golubeva | CLAM | above melting | 1e+23 – 1e+24 [D pulsed high heat plasma loading, 0.6 MJ/m2, 1 ms] | in 1 pulse big uncertainity; 5 pulses (see "ion flux" column) | - | 2.3e+20 |
R6099 | - | Golubeva | F82H | above melting | 1e+23 – 1e+24 [D pulsed high heat plasma loading, 0.6 MJ/m2, 1 ms] | in 1 pulse big uncertainity; 1 and 5 pulses (see "ion flux" column) | - | 5.6e+19 – 7.8e+19 |
R6098 | - | Golubeva | Eurofer | above melting | 1e+23 – 1e+24 [D pulsed high heat plasma loading, 0.6 MJ/m2, 1 ms] | in 1 pulse big uncertainity; 1 and 5 pulses (see "ion flux" column) | - | 2e+20 – 8e+20 |
R6097 | - | Golubeva | Rusfer | above melting | 1e+23 – 1e+24 [D pulsed high heat plasma loading, 0.6 MJ/m2, 1 ms] | in 1 pulse big uncertainity; 1 and 5 pulses (see "ion flux" column) | - | 9.6e+20 – 1e+21 |
R6096 | - | Golubeva | CLAM | below melting | 1e+23 – 1e+24 [D pulsed high heat plasma loading, 0.3 MJ/m2, 1 ms] | in 1 pulse big uncertainity; 1 and 5 pulses (see "ion flux" column) | - | 1.8e+20 – 2.3e+20 |
R6070 | - | Jacob | Eurofer EUROFER-97-2 heat 993 393 | 320 | 5e+19 | 5e+23 | - | - |
R6075 | doi | Jacob | Eurofer | 350 | 1e+19 | 1e+24 | - | - |
R6074 | doi | Jacob | Eurofer | 330 | 1e+19 | 1e+24 | - | - |
R6073 | doi | Jacob | Eurofer | 320 | 1e+19 | 1e+24 | - | - |
R6072 | - | Jacob | Eurofer | 320 | 5e+19 | 1e+24 | - | - |
R6071 | - | Jacob | Eurofer | 320 | 5e+19 | 9e+23 | - | - |
R6102 | - | Makhlai | Eurofer | 500 | 1e+22 | 1e+26 | - | - |
R6103 | - | Makhlai | Eurofer | 500 | 1e+22 | 1e+26 | - | - |
R6104 | - | Makhlai | Eurofer | 500 | 1e+22 | 1e+26 | - | - |
R6105 | - | Makhlai | Rusfer | 500 | 1e+22 | 1e+26 | - | - |
R6106 | - | Makhlai | Rusfer | 500 | 1e+22 | 1e+26 | - | - |
R6060 | - | Nishijima | CLF-1 | 373 | 1.5e+21 – 2e+21 | 1e+25 | - | 1.3e+21 |
R6061 | - | Nishijima | Eurofer | 373 | 1.5e+21 – 2e+21 | 1e+25 | - | 7.87e+19 |
R6062 | - | Nishijima | F82H | 373 | 1.5e+21 – 2e+21 | 1e+25 | - | 4.5e+19 |
R6063 | - | Nishijima | Rusfer | 373 | 1.5e+21 – 2e+21 | 1e+25 | - | 7.99e+20 |
R6064 | - | Nishijima | CLF-1 | 523 | 1.5e+21 – 2e+21 | 1e+25 | - | 4.04e+19 |
R6065 | - | Nishijima | Rusfer | 373 | 1.5e+21 – 2e+21 | 2e+23 | - | 6.5e+21 |
R6066 | - | Nishijima | Rusfer | 373 | 1.5e+21 – 2e+21 | 2e+24 | - | 1.3e+21 |
R6067 | - | Nishijima | Rusfer | 373 | 1.5e+21 – 2e+21 | 4e+25 | - | 1e+21 |
R6059 | - | Terentyev | Eurofer-2 Bohler | 450 | 8e+23 | 5e+25 | - | - |
R6078 | - | Wang | EUROFER97 | 450 – 470 | 2e+21 | 7e+24 | - | - |
R6076 | - | Wang | CLF-1 | 450 – 470 | 2e+21 | 7e+24 | - | - |
R6077 | - | Wang | CLAM | 450 – 470 | 2e+21 | 7e+24 | - | - |
R6082 | - | Wang | EUROFER97 | 450 – 470 | 2e+21 | 7e+24 | - | - |
R6079 | - | Wang | Rusfer | 450 – 470 | 2e+21 | 7e+24 | - | - |
R6080 | - | Wang | CLF-1 | 450 – 470 | 2e+21 | 7e+24 | - | - |
R6081 | - | Wang | CLAM | 450 – 470 | 2e+21 | 7e+24 | - | - |
R6090 | - | Wang | EUROFER97 | 450 – 470 | 2e+21 | 7e+24 | - | 2e+18 |
R6089 | - | Wang | CLAM | 450 – 470 | 2e+21 | 3e+24 | - | 1.4e+19 |
R6088 | - | Wang | CLF-1 | 450 – 470 | 2e+21 | 7e+24 | - | 4.5e+18 |
R6087 | - | Wang | Rusfer | 450 – 470 | 2e+21 | 7e+24 | - | 2e+18 |
R6086 | - | Wang | EUROFER97 | 450 – 470 | 2e+21 | 7e+24 | - | 5e+18 |
R6085 | - | Wang | CLAM | 450 – 470 | 2e+21 | 2e+24 | - | 2.4e+18 |
R6084 | - | Wang | CLF-1 | 450 – 470 | 2e+21 | 2e+25 | - | 1.5e+18 |
R6083 | - | Wang | Rusfer | 450 – 470 | 2e+21 | 7e+24 | - | - |
R6069 | - | Zhou | CLF-1 | 570 | 6.1e+20 | 6e+23 | - | 1.44e+20 |
R6068 | - | Zhou | CLF-1 | 550 | 1e+21 | 6e+23 | - | 2.55e+20 |