Home > Steel Surfaces CRP Experiments > R6099
Contact name | Golubeva | |
Steel type | F82H | |
Ion flux | φ /m-2.s-1 | 1e+23 – 1e+24 [D pulsed high heat plasma loading, 0.6 MJ/m2, 1 ms] |
Ion fluence | Γ /m-2 | in 1 pulse big uncertainity; 1 and 5 pulses (see "ion flux" column) |
Ion energy per D | E /eV | 20 – 30 |
Sample thickness | t /mm | 1 |
Sample temperature | T /K | above melting |
Sample temperature measurement location | backside; heat transfer to cooling system | |
Analysis method | TDS | |
Retained deuterium | Dtot /m-2 | 5.6e+19 – 7.8e+19 |
Image files | Fig_4_AG.jpg, Fig_Total_Ret_AG.jpg |